Table 3 Corrosion parameter values of different substrates exposed to 30 mM H2O2
Substrates | Conditions | Impedance parameters (n = 3) | ||||||
|---|---|---|---|---|---|---|---|---|
Rp | Y0-CPEQp | n | Rt | Y0-CPEQt | n | χ2 | ||
cp-Ti | H2O2 = 0 mM | 7.4E5 (2.0E5) | 5.3 | 0.87 |  |  |  | 10−3 |
cp-Ti | H2O2 = 30 mM | 1.3E−1 (4.5E−2) | 3.8 | 0.93 |  |  |  | 10−3 |
Ti-SLA | H2O2 = 30 mM | 1.0E−1 (5.0E−3) | 4.8 | 0.93 |  |  |  | 10−3 |
Ti-NW | H2O2 = 30 mM | 3.5E−1 (5.8E−2) | 4.9 | 0.92 | 34.6 (6.6) | 4.4E−4 | 1 | 10−3 |
Ti-NW-Zn | H2O2 = 30 mM | 3.1E0 (7.1E−1) | 4.2 | 0.92 | 30.6 (3.4) | 4.5E−4 | 1 | 10−3 |
ANOVA | p < 0.01 | – | – | – |  |  |  | |